1.1133 20Mn5

 

1.1133 exhibit fair machinability, fair to good weldability, and excellent cold formability. Cold drawing markedly increases the tensile strength of this grade. The higher manganese content of 1.1133 steel makes this steel more likely to meet required specifications for heat treatment and better adapted for use in larger sections
 
Composition:

 

%C %Si %Mn %P %S Cr Mo Ni other
0,17-0,23 0,60 1,00-1,50 0,035 0,030 ≤0,40 – – Al 0,015-0,050

 

Hot working:

Forging temperature range: 1260-850℃

Note: Heat to 1260 ℃. Do not forge below 850.

Heat treatment:

Soft annealing ℃ HB 30-soft annealed Normalizing ℃ Hardening temperature for quenching in Water ℃ Hardening temperature for quenching in Oil ℃ Tempering temperature ℃
650-700 – 850-880 820-850 830-860 550-660

 

Main application:

Arbors and discs of large cross section

Shape of product:

Round, flat, step shape, ring, disc, shaft, other shape depend on customer needs